XTRASEAL HI-TEMP GASKET MAKER RTV SILICONE RED 650’F (85 GM)

XTRASEAL HI-TEMP GASKET MAKER RTV SILICONE RED 650'F (85 GM)

XTRASEAL 650°F RED RTV GASKET MAKER IS A ONE PART SILICONE SEALANT WHICH CURE TO FORM A DURABLE RUBBER SEAL THAT OFFER EXCELLENT ADHESION, HEAT RESISTANT FOR GLAZING AND JOINT SEALING APPLICATION.

FEATURES:
– ACETIC ACID CURING SYSTEM.
– OUTSTANDING HIGH TEMPERATURE RESISTANT UPTILL 210°C.
– EXCELLENT GUNNABILITY (-20°C TO 50°C).
– LOW SHRINKAGE.
– NO SAGGING.
– PRIMERLESS ADHESION TO MOST MATERIALS.

USES:
– HIGH TEMPERATURE RESISTANT GASKET AND JOINT SEALING.
– SEALING OF INDUSTRIAL OVENS.
– FORMING IN PLACE GASKETING APPLICATIONS.
– ASSEMBLIES OF GLASS, PORCELAIN COATED METAL, EPOXY AND POLYESTER PANELS, POLYSTYRENE, ANODISED ALUMINIUM, STAINLESS STEEL, FINISHED METAL SURFACE AND FINISHED WOOD.

APPLICATION:
– REMOVE OLD GASKET MATERIAL FROM SURFACES THROUGHLY.
– CLEAN SURFACE WITH RESIDUE-FREE SOLVENT AND ALLOW SURFACE TO DRY.
– CUT NOZZLE TO DESIRED SIZE.
– SQUEEZE TUBE TO FORM A CONTINOUS AND EVEN BEAD TO THE PERIMETER OF MATING SURFACE AND ALL BOLT HOLES.
– TOOL WITHIN 5 MINUTES.
-TIGHTENED TO THE REQUIRED TORQUE, DO NOT OVERTIGHTEN.
-CLEAN OFF EXCESS SEALANT WITH M.E.K. OR TOLUENE.

CURING TIME:
650°F RED RTV SILICONE WILL TACK FREE IN APPROXIMATELY 30 MINUTES AND WILL CURE TO A DEPTH OF 10mm WITHIN 7 DAYS. LONGER CURING TIME MAY BE NECESSARY IN DRY AND LOW HUMIDITY AREA

SPECIFICATION:
CURING SYSTEM : ACETOXY
APPEARANCE : NON-SAGGING PASTE
ODOUR : VINEGAR SMELL
SPECIFIC GRAVITY : 1.01 ± 0.03
SHORE A HARDNESS : >20.
ELONGATION : >300%.
TENSILE STRENGTH : > 1.00MPa.
TOOLING TIME : 5 0MINUTES
TACK FREE TIME : 30 MINUTES
APPLICATION TEMP. : -20°C TO 50°C
CONTINOUS SERVICE TEMPERATURE : -40°C TO 190°C.
INTERMITTENT SERVICE TEMP. : -40°C TO 210°C.
SHELF LIFE : 12 MONTHS
 

STORAGE:
MATERIAL SHOULD BE STORED IN A DRY AND COOL PLACE BETWEEN +50C TO +300C.